| Item | Technical Index | ||
| JC/T 2252-2014 (primer coating) | TH-501H | ||
| Viscosity (mPa.s) | component A | 40±10% | 40 |
| component B | 25±10% | 25 | |
| Surface drying time (h) | ≤4 | 1 | |
| Hard working time (h) | ≤24 | 8 | |
| Solid content (%) | ≥40 | 55 | |
| Bond strength (MPa) | Dry base surface (MPa) | ≥2.5 | 10 |
| Retention rate after immersion (%) | ≥70 | 85 | |
| Peel strength (N/mm) | Dry base surface (N/mm) | ≥6.0 | 7.5 |
| Retention rate after heat aging (%) | ≥70 | 80 | |
| Retention rate after freeze-thaw cycle (%) | ≥70 | 80 | |
| The versatility of spray polyurea products |
| Product shelf life and storage: 1. The storage temperature should be 5-40ºC 2. Under normal storage and transportation conditions, the storage period is not less than 6 months from the date of production 3. Store in a cool, ventilated environment, avoid direct sunlight, prohibit close to fire sources, and prevent collisions 4. Packaging: component A: 220KG/drum, component B: 210KG/drum |
| Precautions: 1. During construction, the temperature of the substrate must be 3°C higher than the dew point temperature; 2. Before the product is used, component B should be fully stirred; 3. The system has a 100% solid content, and it is strictly forbidden to add any diluent; 4. During construction in a confined space, good ventilation must be maintained; 5. When using this product, you must wear work clothes, goggles, gas masks, gloves and other protective equipment. |
| Product application guidance: Recommended spraying machine: Graco H-XP3 polyurea spraying equipment spray gun; air or mechanical self-cleaning polyurea spray gun Static pressure 2300-2500psi; dynamic pressure 2000-2200psi Recommended dry film thickness: 1000-3000μm Recoating interval≤6h |
| Proportion: Component A: Component B =1:1 |